點擊圖片查看大圖現(xiàn)貨供應(yīng)食品級ABS 沙伯基礎(chǔ) CYCOLAC MG47F
Multi-purpose, injection molding ABS providing a favorable balance of engineering properties. FDA compliant.
多用途，注塑ABS提供了良好的工程性能平衡。符合FDA。
MG47F物性表：
| REVISION: 09/07/2019 Compare this region | ||||
|---|---|---|---|---|
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 44 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 33 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 24 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2270 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 70 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D 790 | |
| Hardness, Rockwell R | 112 | - | ASTM D 785 | |
| Tensile Stress, yield, 50 mm/min | 47 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 35 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 2.6 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | 25 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 2370 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 70 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2200 | MPa | ISO 178 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 320 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 30 | J | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 22 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 26 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m2 | ISO 179/1eA | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 99 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 94 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 80 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 8.82E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 8.82E-05 | 1/°C | ASTM E 831 | |
| Vicat Softening Temp, Rate B/50 | 98 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 100 | °C | ISO 306 | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 81 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 80 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 80 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 80 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.04 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.8 | % | SABIC method | |
| Melt Flow Rate, 230°C/3.8 kg | 5.6 | g/10 min | ASTM D 1238 | |
| Melt Viscosity, 240°C, 1000 sec-1 | 2250 | Poise | ASTM D 3825 | |
| Density | 1.04 | g/cm3 | ISO 1183 | |
| Melt Flow Rate, 220°C/10.0 kg | 18 | g/10 min | ISO 1133 | |
| ELECTRICAL | ||||
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | ||||
| UL Yellow Card | E45329-102071279 | - | - | |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 | |
| INJECTION MOLDING | ||||
| Drying Temperature | 80-95 | °C | ||
| Drying Time | 2-4 | hrs | ||
| Drying Time (Cumulative) | 8 | hrs | ||
| Maximum Moisture Content | 0.1 | % | ||
| Melt Temperature | 220-260 | °C | ||
| Nozzle Temperature | 220-260 | °C | ||
| Front - Zone 3 Temperature | 215-240 | °C | ||
| Middle - Zone 2 Temperature | 205-225 | °C | ||
| Rear - Zone 1 Temperature | 190-210 | °C | ||
| Mold Temperature | 50-70 | °C | ||
| Back Pressure | 0.3-0.7 | MPa | ||
| Screw Speed | 30-60 | rpm | ||
| Shot to Cylinder Size | 50-70 | % | ||
| Vent Depth | 0.038-0.051 | mm | ||