VALOX ? Resin 357X

SI | British | Metric | PDF Europe-Africa-Middle East: COMMERCIAL

 
VALOX 357X is an impact modified, flame retarted PBT+PC blend. Applications like bobbins, switches and enclosures.
 

Property
 
TYPICAL PROPERTIES (1)
MECHANICAL Value Unit Standard
Tensile Stress, yld, Type I, 50 mm/min 500 kgf/cm2 ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min 400 kgf/cm2 ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min 5 % ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min 30 % ASTM D 638
Tensile Modulus, 50 mm/min 20300 kgf/cm2 ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 790 kgf/cm2 ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 21400 kgf/cm2 ASTM D 790
Taber Abrasion, CS-17, 1 kg 33 mg/1000cy SABIC Method
Tensile Stress, yield, 50 mm/min 50 MPa ISO 527
Tensile Stress, break, 50 mm/min 40 MPa ISO 527
Tensile Strain, yield, 50 mm/min 5 % ISO 527
Tensile Strain, break, 50 mm/min 30 % ISO 527
Tensile Modulus, 1 mm/min 2200 MPa ISO 527
Flexural Stress, yield, 2 mm/min 80 MPa ISO 178
Flexural Modulus, 2 mm/min 2000 MPa ISO 178
Hardness, H358/30 115 MPa ISO 2039-1
Hardness, Rockwell R 115 - ISO 2039-2
IMPACT Value Unit Standard
Charpy Impact, unnotched, 23°C NB kJ/m2 ISO 179/2C
Charpy Impact, unnotched, -30°C NB kJ/m2 ISO 179/2C
Izod Impact, unnotched, 23°C NB cm-kgf/cm ASTM D 4812
Izod Impact, unnotched, -30°C NB cm-kgf/cm ASTM D 4812
Izod Impact, notched, 23°C 50 cm-kgf/cm ASTM D 256
Izod Impact, notched, 0°C 19 cm-kgf/cm ASTM D 256
Izod Impact, notched, -30°C 15 cm-kgf/cm ASTM D 256
Instrumented Impact Total Energy, 23°C 356 cm-kgf ASTM D 3763
Izod Impact, unnotched 80*10*4 +23°C NB kJ/m2 ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C NB kJ/m2 ISO 180/1U
Izod Impact, notched 80*10*4 +23°C 40 kJ/m2 ISO 180/1A
Izod Impact, notched 80*10*4 0°C 20 kJ/m2 ISO 180/1A
Izod Impact, notched 80*10*4 -30°C 15 kJ/m2 ISO 180/1A
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 45 kJ/m2 ISO 179/1eA
Charpy Impact, notched, 23°C 40 kJ/m2 ISO 179/2C
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm 20 kJ/m2 ISO 179/1eA
Charpy Impact, notched, -30°C 20 kJ/m2 ISO 179/2C
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m2 ISO 179/1eU
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm NB kJ/m2 ISO 179/1eU
THERMAL Value Unit Standard
Vicat Softening Temp, Rate A/50 180 °C ASTM D 1525
Vicat Softening Temp, Rate B/50 145 °C ASTM D 1525
HDT, 0.45 MPa, 3.2 mm, unannealed 130 °C ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed 85 °C ASTM D 648
CTE, -40°C to 40°C, flow 9.18E-05 1/°C ASTM E 831
CTE, -40°C to 40°C, xflow 8.4E-05 1/°C ASTM E 831
Thermal Conductivity 0.17 W/m-°C ISO 8302
CTE, 23°C to 80°C, flow 1.E-04 1/°C ISO 11359-2
CTE, 23°C to 80°C, xflow 1.E-04 1/°C ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C PASSES - IEC 60695-10-2
Vicat Softening Temp, Rate A/50 180 °C ISO 306
Vicat Softening Temp, Rate B/50 145 °C ISO 306
Vicat Softening Temp, Rate B/120 150 °C ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm 135 °C ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm 85 °C ISO 75/Ae
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm 130 °C ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 85 °C ISO 75/Af
Relative Temp Index, Elec 120 °C UL 746B
Relative Temp Index, Mech w/impact 120 °C UL 746B
Relative Temp Index, Mech w/o impact 140 °C UL 746B
PHYSICAL Value Unit Standard
Specific Gravity 1.34 - ASTM D 792
Mold Shrinkage on Tensile Bar, flow (2) (5) 1.1 - 1.8 % SABIC Method
Mold Shrinkage, flow, 3.2 mm (5) 1 - 1.4 % SABIC Method
Mold Shrinkage on Tensile Bar, xflow (2) (5) 0.9 - 1.8 % SABIC Method
Melt Flow Rate, 250°C/5.0 kgf 9.6 g/10 min ASTM D 1238
Melt Flow Rate, 265°C/5.0 kgf 13 g/10 min ASTM D 1238
Melt Flow Rate, 266°C/5.0 kgf 13 g/10 min ASTM D 1238
Density 1.34 g/cm3 ISO 1183
Water Absorption, (23°C/sat) 0.5 % ISO 62
Moisture Absorption (23°C / 50% RH) 0.15 % ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg 8 cm3/10 min ISO 1133
Melt Volume Rate, MVR at 265°C/5.0 kg 10 cm3/10 min ISO 1133
Melt Viscosity, 260°C, 1500 sec-1 310 Pa-s ISO 11443
ELECTRICAL Value Unit Standard
Volume Resistivity >1.E+15 Ohm-cm ASTM D 257
Dielectric Strength, in oil, 1.6 mm 25 kV/mm ASTM D 149
Dielectric Strength, in oil, 3.2 mm 17 kV/mm ASTM D 149
Relative Permittivity, 1 MHz 3 - ASTM D 150
Dissipation Factor, 1 MHz 0.013 - ASTM D 150
Arc Resistance, Tungsten {PLC} 6 PLC Code ASTM D 495
Hot Wire Ignition {PLC) 3 PLC Code UL 746A
High Voltage Arc Track Rate {PLC} 3 PLC Code UL 746A
High Ampere Arc Ign, surface {PLC} 0 PLC Code UL 746A
Comparative Tracking Index (UL) {PLC} 3 PLC Code UL 746A
Volume Resistivity >1.E+15 Ohm-cm IEC 60093
Surface Resistivity, ROA >1.E+15 Ohm IEC 60093
Dielectric Strength, in oil, 0.8 mm 34 kV/mm IEC 60243-1
Dielectric Strength, in oil, 1.6 mm 25 kV/mm IEC 60243-1
Dielectric Strength, in oil, 3.2 mm 17 kV/mm IEC 60243-1
Relative Permittivity, 1 MHz 3 - IEC 60250
Dissipation Factor, 50/60 Hz 0.002 - IEC 60250
Dissipation Factor, 1 MHz 0.001 - IEC 60250
Comparative Tracking Index 225 V IEC 60112
Comparative Tracking Index, M 100 V IEC 60112
Relative Permittivity, 50/60 Hz 3 - IEC 60250
FLAME CHARACTERISTICS Value Unit Standard
UL Recognized, 94V-0 Flame Class Rating (3) 0.75 mm UL 94
UL Recognized, 94-5VA Rating (3) 2.5 mm UL 94
Glow Wire Flammability Index 960°C, passes at 1 mm IEC 60695-2-12
Glow Wire Ignitability Temperature, 1.0 mm 825 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm 725 °C IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm 700 °C IEC 60695-2-13
Oxygen Index (LOI) 30 % ISO 4589
Source GMD, last updated:2016/02/03
Processing

Parameter
Injection Molding Value Unit
Drying Temperature 110 - 120 °C
Drying Time 2 - 4 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250 - 270 °C
Nozzle Temperature 240 - 260 °C
Front - Zone 3 Temperature 245 - 265 °C
Middle - Zone 2 Temperature 240 - 255 °C
Rear - Zone 1 Temperature 230 - 245 °C
Hopper Temperature 40 - 60 °C
Mold Temperature 40 - 100 °C
Source GMD, last updated:2016/02/03
上一篇： 暫無相關(guān)信息！

轉(zhuǎn)載請注明：轉(zhuǎn)載自環(huán)球塑化資訊網(wǎng) http://m.hg3236.com/news/
本文鏈接：http://m.hg3236.com/b-shabo/news269818/
免責(zé)聲明：本文"PBT+PC VALOX ? Resin 357X"僅代表作者個人觀點(diǎn)，與環(huán)球塑化網(wǎng)無關(guān)。環(huán)球塑化網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請與我們聯(lián)絡(luò)。電話：400-115-2868

機(jī)械手 激光機(jī)
©2024 環(huán)球塑化網(wǎng) 版權(quán)所有   技術(shù)支持： 環(huán)球塑化網(wǎng)     訪問量：522734  管理入口

收縮

  • 電話咨詢

  • 0769-82558310
QR code
關(guān)閉
關(guān)閉
請輸入驗證碼