PC/PET 基礎(chǔ)創(chuàng)新塑料(美國) XYLEX X8300 物性介紹:
未增強(qiáng)級PC/PET合金;高流動性;抗沖擊性;良好的耐化學(xué)性;透明度高、卓越的光學(xué)性能;紫外線穩(wěn)定。
PC/PET SABIC基礎(chǔ)創(chuàng)新塑料(美國) XYLEX X8300 主要應(yīng)用:
手機(jī)外殼和透鏡、個人數(shù)字產(chǎn)品、其他外圍設(shè)備;室外活動場所用的頂蓋和構(gòu)件、滑雪板緊固件、防護(hù)裝置;汽車"高接觸"內(nèi)部元件(按鈕、手柄)。
XYLEX X7300 Resin Polycarbonate + Polyester Supplied by SABIC Innovative Plastics Europe
Product De
PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized.
XYLEX™ 樹脂是將脂肪族聚酯和聚碳酸酯結(jié)合起來,形成一種在延展性、透明性和耐化學(xué)性能間達(dá)到良好平衡的聚合物。XYLEX™ 通過其設(shè)計的靈活性和美學(xué)的多樣性體現(xiàn)了其競爭優(yōu)勢。迄今為止設(shè)計工程師通常選擇的余地不多,但使用XYLEX™ 樹脂后,他們就可以尋求新的設(shè)計方案和機(jī)會。
Bayer MaterialScience Makroblend® UT-250 Polycarbonate + Polyester Blend Key Features:
Unfilled;High impact or high impact modified;Light stabilized or stable to light。
makroblend ®品牌名稱是由拜耳材料生產(chǎn)的聚碳酸酯(PC)和聚對二甲酸丁二醇酯(PBT)或PC和聚對二甲酸乙二醇酯(PET)。Makroblend ®特點(diǎn)是其高韌性,即使在低溫下,良好的耐化學(xué)性,敏感性降低應(yīng)力開裂性,良好的涂飾性和低吸水性。Makroblend ®應(yīng)用程序被發(fā)現(xiàn)在汽車工程,電氣工程/電子,照明等領(lǐng)域的技術(shù)和體育與休閑。Makroblend ®制造單位已獲得DIN ISO 9001和14001認(rèn)證協(xié)會負(fù)責(zé).
PC/PET 基礎(chǔ)創(chuàng)新塑料(美國) XYLEX X8300 原廠物性數(shù)據(jù)表:
TYPICAL PROPERTIES (1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min | 490 | kgf/cm² | ASTM D 638 | |
Tensile Stress, brk, Type I, 50 mm/min | 530 | kgf/cm² | ASTM D 638 | |
Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D 638 | |
Tensile Modulus, 50 mm/min | 18700 | kgf/cm² | ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 840 | kgf/cm² | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 19700 | kgf/cm² | ASTM D 790 | |
Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 | |
Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 | |
Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 | |
Tensile Strain, break, 50 mm/min | >150 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 1900 | MPa | ISO 527 | |
Flexural Stress, break, 2 mm/min | 71 | MPa | ISO 178 | |
Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, notched, 23°C | 67 | cm-kgf/cm | ASTM D 256 | |
Instrumented Impact Total Energy, 23°C | 968 | cm-kgf | ASTM D 3763 | |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A | |
THERMAL | Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50 | 108 | °C | ASTM D 1525 | |
HDT, 0.45 MPa, 3.2 mm, unannealed | 102 | °C | ASTM D 648 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 88 | °C | ASTM D 648 | |
CTE, -40°C to 40°C, flow | 1.15E-04 | 1/°C | ASTM E 831 | |
CTE, -40°C to 40°C, xflow | 1.05E-04 | 1/°C | ASTM E 831 | |
CTE, 23°C to 60°C, flow | 8.5E-05 | 1/°C | ISO 11359-2 | |
CTE, 23°C to 60°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 | |
Vicat Softening Temp, Rate B/120 | 106 | °C | ISO 306 | |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 90 | °C | ISO 75/Ae | |
PHYSICAL | Value | Unit | Standard | |
Specific Gravity | 1.2 | - | ASTM D 792 | |
Mold Shrinkage, flow, 3.2 mm (5) | 0.4 - 0.8 | % | SABIC Method | |
Mold Shrinkage, xflow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method | |
Melt Flow Rate, 265°C/2.16kgf | 21 | g/10 min | ASTM D 1238 | |
Density | 1.18 | g/cm³ | ISO 1183 | |
Melt Volume Rate, MVR at 265°C/2.16 kg | 21 | cm³/10 min | ISO 1133 | |
OPTICAL | Value | Unit | Standard | |
Light Transmission, 2.54 mm | 88 | % | ASTM D 1003 | |
Haze, 2.54 mm | 2 | % | ASTM D 1003 |
|
PC/PET SABIC基礎(chǔ)創(chuàng)新塑料(美國) XYLEX X8300 注塑參數(shù):
Parameter
Injection Molding
Drying Temperature
Drying Time
Drying Time (Cumulative)
Maximum Moisture Content
Melt Temperature
Nozzle Temperature
Front - Zone 3 Temperature
Middle - Zone 2 Temperature
Rear - Zone 1 Temperature
Mold Temperature
Back Pressure
Screw Speed
Shot to Cylinder Size
Vent Depth
東莞鼎鑫塑化以下PC/PET產(chǎn)品本公司長期現(xiàn)貨供應(yīng):
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PET
PC/PBT
PC/PBT
PC/PBT
PC/PBT
PC/PET
PC/PET
PC/PET
PC/PET